Scratch Repair Solutions for uPVC and Aluminium Profiles

Via Crevada, 9/E
31020 - San Pietro di Feletto
Tel. : +390438 4548
C-22/13, Sec-57, Noida - 201301

Scratch Covering on Coloured Profiles
Scratch Filling with Wax Putty on White Profiles
Made In Italy
New Products from Europe Distributed In India by...
VRTS INDUSTRIAL SOLUTIONS PVT. LTD.
C-22/13, Sec-57, Noida-201301
E.: info@vrts.co.in | W.: www.vrts.co.in
M.: +91 96500 11947
&
Paint for uPVC and Aluminium Proles
Filler Tools & Wax Putty
Touch - Up Pens
Filler Tools Wax Putty Touch - Up Pen
Available In Any Shades Of White Or RAL Colours
Scratch Filling with Wax Putty on Coloured Profiles
Scratches on uPVC Doors & Windows ?... We have the Solutions !!
Easy, Quick & Reliable European Technology, Now Available in India

FINITURA ADP
Finish with direct adhesion to PVC, ABS and PC/ABS
1846.
11/03/10 LRB/nz
IMPA Spa - Via Crevada 9/E - 31020 San Pietro di Feletto (TV) Italy - tel. +39 0438 4548 - fax 0438 454915 - www.impa.it - info@impa.it
Page 1 / 2
Description and use
Semigloss enamel based on acrylic resin and isocyanate adduct.
Recommended for use on properly prepared plastic substrates.
It can be coloured using the ADVANCE HT/IMPASYSTEM tinting system.
Technical data
Colour : on request
Pot-life : 4 ÷ 6 hours
Dry film appearance : semigloss - 45 ÷ 60 gloss (Gardner 60°) depending
on thickness.
Viscosity : Part “A” : 60 ÷ 80 seconds ISO-DIN Cup # 4
Practical cover rate∗
: 8 ÷ 9 m²/kg per two coats.
Storage life : 12 months in original sealed container.
∗
The cover rate is calculated on the suggested thickness and applied on plane and regular surfaces.
NB: Data recorded @ 20°C.(68°F.)
Substrate preparation
PVC/ABS/PC/ABS: clean and degrease by using ANTISILICONE code 1618, then pass with a cloth
soaked of DILUENTE EXTRA PU code 1611, wait until the surface becomes matt, next apply
FINITURA ADP.
TRANSPARENT PLEXIGLASS: clean only using ANTISILICONE.
Preparation
Stir thoroughly the product to achieve even colour and consistency, then add the suitable hardener
in the following ratio:
BY WEIGHT / IN PESO
PRODUCT / PRODOTTO
1846 FINITURA ADP
100
HARDENER / INDURITORE
4300 INDURITORE STANDARD or else/oppure
4500 INDURITORE FAST
20
THINNER / DILUENTE
1611 DILUENTE EXTRA PU or else/oppure
1653 DILUENTE PER ACRILICI
15 ÷ 20
Application method : - air mix spray gun with nozzle ∅ 1.2 ÷ 1.4 mm and
pressure of 3 ÷ 4 bar.
Recommended thickness : 30 μm dry film in two-three layers, waiting 5 ÷ 10
minutes between them.

FINITURA ADP
Finish with direct adhesion to PVC, ABS and PC/ABS
1846.
11/03/10 LRB/nz
This note replaces all the previous ones. Please, make sure to have the latest issue. The above mentioned data are meant to facilitate our customers in the use of our
products. IMPA is not responsible for applications of products carried out beyond its direct control.
Page 2 / 2
DRYING TIME / ESSICCAZIONE
Dust free
Fuori polvere
Handling
Al tatto
Through drying
In profondità
Air drying/Aria @ 20°C.65%R.H./U.R. 15 ÷ 20 minutes/min. 4 ÷ 6 hours/ore
24 ÷ 36
hours/ore
Oven/Forno @ 60°C.
Flash off/ Appassimento: 20 ÷ 30 min. 50 ÷ 60 minutes
NOTE: Apply only the suggested thickness. Otherwise, and especially in case of high environment
temperature, blisters may come up on the film surface.
Do not apply the product after the suggested pot-life; the forming film will have bad adhesion to the
substrate.
Information provided in this technical data sheet is based upon our best experience and technical
knowledge; it does not absolve the users from carrying out tests and preventive checks in order to
verify the suitability for use. For further technical information about specific systems and/or special
applications, please contact our TECHNICAL SERVICE.
FOR PROFESSIONAL USE ONLY

BARRIER 87-1151 0704.
Water-reducible Intumescent Paint
02/10/13 LRC/nz
Description and use
Intumescent Paint for fire protection of metal structures, metal panels, columns and structures made
up of cement, concrete floors, brick walls, etc.
In case of fire, special BARRIER 87-1151 components interact at temperatures above 200°C
(390°F), producing a non-flammable insulating foam that protects the surface from fire for some time,
preventing the structural elements from subsiding, and allowing the fire brigade to intervene and
possibly to access the blazing premises without the risk of a structural collapse.
The time for which the BARRIER protects against fire is shown in minutes and represents the
"Class" of the product.
This varies depending on the type of surface and on the thickness of the BARRIER applied.
It is recommended to protect structures indoors or not directly exposed to washing away of the rain
or to high humidity such as steel or concrete industrial buildings, warehouses, canopies, cinemas,
theatres, schools, hospitals, airports, underground stations, etc.
Technical data
Colour :white. For technical reasons BARRIER can't be
produced in deep colours. It's possible to get it into light
shades or it can be recoated to obtain the required final
colour.
Binder
Dry film appearance
Total non volatile by weight
Specific gravity @ 20°C
Viscosity @ 20°C
Practical coverage
Storage life
: vinyl versatate dispersion
: matt
: 66% ( ± 1)
: 1.29 kg/l ( ± 0.04)
: 4800  6400 mPa.s Brookfield RVT rpm 50 s 5
: according the requested resistance class.
: 12 months in original sealed container.
NB: The storage and application temperature must be kept within + 5°C(41°F) and + 25°C (77°F)
This product is Compliant with fire protection requirement for passenger vehicles
according to FMVSS 302-2008. Product certification issued by Automotive Research
Association - ARAI in 2013
Compliant with Directive 2004/42/CE-IIA(i) maximum VOC limit value: 140 g/l (2010)
Application note
Surface preparation : BARRIER can be applied directly on the surfaces to be
protected, provided that they are clean, dry, without
dust or grease and made rough by sanding or sand-
blasting. On steel surfaces apply a first light coat of a
quick drying antirust paint FONDO F.D. code 1859 or
KORINTHOS PRIMER code 0717 or FONDO
ANTICORROSIVO EPOX code 1293. On galvanized
steel, use as an adhesion primer our product
KORINTHOS PRIMER or FONDO
ANTICORROSIVO EPOX.
In case of chalking or fresh concrete, surface must be
treated with a layer of fixative masonry sealer CLIM-O-
Page 1 / 4

BARRIER 87-1151 0704.
02/10/13 LRC/nz
PAINT PRO code 1004, or with a water-thinnable type
POLY ACRYL code 0004 or SUPERFIX code 0010.
Product preparation : Mix well to even colour and consistency.
Application method : - airless spraying - air mix - roller - brush
Reduction : BARRIER is ready to use and should be applied such it
is just to make a sufficient thickness with less possible
paint layers.
If necessary and according to the application method,
BARRIER can be thinned down with 5  10% of water.
Application : - airless spraying: we recommend the use of a high
pressure piston or diaphragm pump, gas or electric
engine powered (200  250 bar). Choose self-cleaning
nozzle and spraying angle according to the structure to
be treated but not less than 23 (0.023 inch = 0.58 mm).
The angle of the spray nozzle is very important in order
to limit waste spraying.
- conventional spray gun: use nozzles with large hole
∅ 2.2  2.5 mm @ 3  5 bar pressure.
Air drying time : According to the applied thickness.
In ventilated place, at 25°C one coat of 600 µmwet will
be recoatable after few hours and will be completely dry
after approx. 24 hours.
Suggested thickness : Thickness changes depending on requested protection
"Class". Thickness and relative protections (steel or
concrete) are well indicated in the Test Certificate.
Described thickness must be respected without
exceeding, particularly in the corners where too much
product can crack during drying time.
Apply product in several coats. Do not apply more than
700  800 µmwetforeachsinglecoat.Onesinglecoat
of 800 µmwetcanbeappliedwithairlesspumpandit
correspond to 550 µmdry=1Kg/m2.
WARNING: Contact our TECHNICAL SERVICE to know the quantity of product to be applied
on the structures to be treated.
Certificates are issued by Afiti Licof (Spain).
Page 2 / 4

BARRIER 87-1151 0704.
02/10/13 LRC/nz
On STEEL STRUCTURES certified for Class R 15 - 30 - 45 - 60 - 90 - 120 (Certificate n°
2125T10-4 of 27/07/2011) issued by Afiti Licof according to the European Standards UNE ENV
13381-8:2010.
On WALLS AND FLOORS certified for Class R 30 - 60 - 90 - 120 (Certificate n°8689/12-2 of
09/10/2012) issued by Afiti Licof according to the European Standards UNE ENV 13381-3:2004.
On BEAMS AND COLUMNS certified for Class R 30 - 60 - 90 - 120 (Certificate n°8689/12-3 of
09/10/2012) issued by Afiti Licof according to the European Standards UNE ENV 13381-3:2004.
On request, integrative reports are worded by an engineer enrolled in the official list of the Ministry of
the Interiors, according to law n°818-84.
In accordance with Directive 89/106/EEC on construction products, Barrier 87-1151 has been
awarded the European Technical Approval (ETA) and EC mark for compliance with the provisions of
ETAG 018 Guidelines - part 1 and part 2.
INSTRUCTIONS FOR CONSERVATION AND APPLICATION OF "BARRIER" WATER-BASED
1 - During storage
Because of the thixotropic features of the product, after long storage there could occur a
thickening. In this case carry out a mechanical stirring by a suitable propeller drill.
Avoid temperature below + 5°C (41°F), frozen product can not be used anymore. (BEWARE
OF FROST). Avoid storage for long time at temperature over 25°C (77°F).
2 - During application
Applying BARRIER outdoor, in open air and in several days, it is absolutely necessary to
protect coated surfaces from rain and dew 'till recoating them with a water-proof paint.
No caution needed if product will be applied indoor and in a dry place like cinemas, theatres,
schools, garages, closed hangars, shopping centres, supermarkets, etc.
3 - After application
Avoid washing away by the rain which, because of BARRIER porosity, will go through the film
coat getting blisters and flaking, and also dissolving and taking off the active components,
leaving the product absolutely inefficient against the fire.
Also high moisture or steam will get problems time by time (for example for application in
shower room, laundry, dungeon, etc.) because the dampened salts will be partially dissolved,
coming up on the surface and causing, after some time, superficial crusts.
In such conditions BARRIER must be always protected, overcoating it with a water-proof
paint.
Apply a protective water-proof coat in the properly thickness, without exceed in quantity
because high thickness may stop the free foam expansion in fire conditions.
At the end of the coating system, BARRIER will not be sensitive anymore to even strong
sudden changes of temperature. Applied product will not loose its intumescent features,
Page 3 / 4

BARRIER 87-1151 0704.
02/10/13 LRC/nz
provided that there will not happen one of the above described conditions, and the
application has be done following exactly all the instructions.
NOTE: Information provided in this technical data sheet is based upon our best experience and
technical knowledge; it does not absolve the users from carrying out tests and preventive checks in
order to verify the suitability for use. For further technical information or for suggestions about
specific systems and/or applications, please contact our TECHNICAL SERVICE.
Page 4 / 4

INSONORIZZANTE ANTIVIBRAZIONE
Sound damping insulating compound
PR000325
08/05/12 LRA/rz
Page 1 / 2
Description and use
Sound damping and thermal insulating coating that features good adhesion, excellent flexibility and
with high mechanical and chemical resistance.
It’s a water based viscous elastic compound that does not contain flammable or harmful solvents and
thanks to its very slight odour, it is suitable for applications in closed rooms.
After drying, it can be overcoated with any kind of finishing coat, water or solvent-based.
The adhesion is good to different kind of substrate as steel, galvanized sheet, aluminium, wood,
glass, fibreglass and some plastic surfaces.
The product can be used on marine as well as Industry vehicles (cars, buses and train bodies, ship
hulls, engine compartments, pipes ) to dampen unwanted noises generated from sources of
vibration. It gives protection against condensation, it is fire-retardant and thermal insultation.
Technical data
Colour : grey
Dry film appearance : coarse, matt
Suggested thickness : first coat up to 3 mm wet film. A second coat can be
applied with thickness up to 4-5 mm wet film (if
needed).
Specific gravity : 1.07 kg/l ( ± 0.02)
Viscosity : 35000 ÷ 50000 mPa*s Brookfield RVT rpm 20 s 7
Practical coverage : 1,5-4kg/m² referred to thickness of 1,0-2,5 mm (dry film)
Heat proof : max. 100 °C
Damping factor ASTM E756-4 : 2,5 ɳ @ 200Hz 20°C
Thermal transmittance UNI EN ISO 6946 : 0,165 W/m.K
Sound absorption ASTM E1050 : α 0,3 -0,4 (thickness 4 mm)
Storage life : 12 months in original sealed container.
NB: Data recorded @ 20°C (68°F)
The product is compliant with Directive 2004/42/CE-IIB(e) maximum VOC limit value: 0,38 g/l
Application note
Substrate preparation : Surfaces must be clean, dust free, without oil or grease
traces.
Product preparation : the product will appear thick. Before use, it is necessary
to mix well for some minutes with a slotted paddle to
achieve a smooth consistency.
Application method : Brush, roller, but it suggested the airless equipment,
spraying with spray gun model LARIUS L91X and Super
fast clean nozzle flow rate 25-40 (with no filter applied).
We suggest to use the following spray equipement
model LARIUS:

INSONORIZZANTE ANTIVIBRAZIONE
Sound damping insulating compound
PR000325
08/05/12 LRA/rz
Page 2 / 2
1.THOR HR electric piston pump
2.SUPER NOVA 68:1 HR pneumatic piston pump.
-brush/roller: suggested on small surfaces with smooth
textured effect.
Reduction : Product ready-to-use. Avoid adding water
Air drying time (25°C,HR 40%) : Dust free : 1,5 hours
with thickness of 2mm wet Touch free : 6 hours
Dry through : 24 hours
NOTE: Drying time can be influenced by:
1. temperature
2. humidity
3. aeration
4. thickness
5. application method
Recoatable : after drying (7 – 14 days), with any kind of car paint.
Pulizia : Clean equipement immediately after use with water and
soap. Avoid material to harden
NOTE:
Do not apply in foggy or rainy weather, or when the relative humidity exceeds 75%.
BEWARE OF FROST. Store the product between + 5 and 30°C.
verify the suitability for use. For further technical information about specific systems and/or special
applications, please contact our TECHNICAL SERVICE.

EPOX MARINE
Epoxy filler paste for finishing
1295.
24/06/10 LRD/nz
Page 1 / 2
Description and uses
Two-pack epoxy filler paste particularly recommended for smoothing.
It is easy to spread also on large surfaces; its main feature is the good sandability and the water
resistance.
The product should be applied on filler paste and epoxy primers.
Technical data
Colour : grey
Appearance of the hardened product : solid mass, strong
Binder : epoxy-polyamide resins
Type of product : 2K with INDURITORE (hardener) code 4053
Specific gravity : Part “A” : 1.54 kg/l ( ± 0.02)
Part “B” : 1.54 kg/l ( ± 0.02)
Curing ratio : 1 : 1 by weight or volume
Pot-life : 90 minutes
Texture : thixotropic paste
Durezza Shore A : 94
Durezza Shore D : 55
Assorbimento a 21 gg - IP AA ST : acqua dolce 0.55%
Ritiro lineare - IP MI RL : < = 0.7%
Storage life : 24 months in original sealed container, away from light.
NB: Data recorded @ 20°C.(68°F.)
Application note
Substrate preparation : Surfaces must be dry, clean, free from dust or grease
and made rough by sanding.
Application method : - spatula - trowel
Reduction : Product is ready-to-use and must not be thinned.
Suggested thickness : from thin layers to a maximum thickness of 3 mm
Hardening : Product remains spreadable for about 1 hour @ 20°C.
(68°F.), then it starts to get viscous and thick, till it is no
more applicable.
The complete hardening and the maximum chemical
resistance will be reached after a week.
Temperature affects strongly the hardening time, and
the differences between summer and winter can be
considerable.
Sandable : after 24 hours @ 20°C.
Overcoatable : immediately after sanding, or between 24 and 36 hours

EPOX MARINE
Epoxy filler paste for finishing
1295.
24/06/10 LRD/nz
Page 2 / 2
Tools cleaning : immediately after use with Cellulose Thinner
To use correctly, take out 1 part by weight or by volume of the component “A” and 1 part of the
component “B”, stir thoroughly up to obtain an homogeneous coloured mass.
Apply making a light pressure with the spatula, in order to allow the filler to enter the unevenness of
the surface, ensuring so a better adhesion.
NOTE:
It is recommended not to use when temperature is below + 10°C.(50°F.) or above 35°C.(95°F.)
verify the suitability for use. For further technical information or for suggestions about specific
systems and/or applications, please contact our TECHNICAL SERVICE.

Scratch Repair Solutions for uPVC and Aluminium Profiles

Recommended

Recommended

More Related Content

What's hot

What's hot (19)

Similar to Scratch Repair Solutions for uPVC and Aluminium Profiles

Similar to Scratch Repair Solutions for uPVC and Aluminium Profiles (20)

More from IndiaMART InterMESH Limited

More from IndiaMART InterMESH Limited (20)

Recently uploaded

Recently uploaded (20)

Scratch Repair Solutions for uPVC and Aluminium Profiles