International Journal of Engineering Research and Development
e-ISSN: 2278-067X, p-ISSN: 2278-800X, www.ijerd.com
Volume 11, Issue 09 (September 2015), PP.72-77
72
Reducing Corrosion Rate by Welding Design
Muhammad Akhlis Rizza
1
, Anang Takwanto
2
1
Mechanical Engineering Dept, State Polytechnic of Malang, Jl. Soekarno Hatta 9 Malang, Indonesia.
2
Chemichal Engineering Dept, ,State Polytechnic of Malang, Jl. Soekarno Hatta 9 Malang, Indonesia.
Abstract:- The paper addresses the importance of welding design to prevent corrosion at steel. Welding is
used to join pipe, profiles at bridges, spindle, and a lot more part of engineering construction. The
problems happened associated with welding are common issues in these fields, especially corrosion.
Corrosion can be reduced with many methods, they are painting, controlling humidity, and also good
welding design. In the research, it can be found that reducing residual stress on the welding can be
solved in corrosion rate reduction problem.
Preheating on 500oC and 600oC give better condition to reduce corosion rate than condition after
preheating 400oC. For all welding groove type, material with 500oC and 600oC preheating after 14 days
corrosion test is 0,5%-0,69% lost. Material with 400oC preheating after 14 days corrosion test is 0,57%-0,76%
lost.
Welding groove also influence corrosion rate. X and V type welding groove give better condition to reduce
corrosion rate than use 1/2V and 1/2 X welding groove. After 14 days corrosion test, the samples with
X welding groove type is 0,5%-0,57% lost. The samples with V welding groove after 14 days corrosion test is
0,51%-0,59% lost. The samples with 1/2V and 1/2X welding groove after 14 days corrosion test is 0,58%-
0,71% lost.
Keywords:- welding, corrosion, pre-heating, residual stress.
I. INTRODUCTION
Corrosion is depravation of essential properties in a material due to reactions with its environment.
Millions of dollars are lost each year because of corrosion. Much of this loss is due to the corrosion of iron and
steel, although many other metals may corrode as well. (Kadry, 2008). Welding process can make some
changes of microstructures, formation of residual stresses due to the non-uniform temperature distribution
during the welding thermal cycle. The changes in microstructures and surface conditions are non-uniform. Each
different zone of a weldment is expected to have different corrosion behavior. (Xiong, Tan, & Forsyth, 2013)
Welding process become very important since almost all of joint in engineering system using various
kind of welding process. Researcher tries to solve side effect of welding process, including corrosion.
The corrosion behaviour and microstructure of Al6061 alloy welded by GTAW (Gas tungsten arc
welding) and followed by various heat treatments have been researched. The microstructure of both weld metal
(WM) and base metal (BM) was investigated using scanning electron microscopy (SEM) and energy
dispersive spectroscopy (EDS). Corrosion behavior was investigated in 3.5 wt.% NaCl aqueous solution. The
results showed that BM consists of Fe-rich coarse intermetallic particles. (Nikseresht, Karimzadeh, Golozar, &
Heidarbeigy, 2010)
Some mechanical properties and corrosion behavior in five zones from the weld metal to base metal of
a 2205 duplex stainless steel joint, which was welded by double-pass tungsten inert gas arc welding with filler
wire was investigated. Results of the research showed that a great deal of secondary austenite appeared in weld
metal due to the reheat of second pass welding and coarse ferrite grains were formed near the fusion line, while
other zones had the similar microstructures with a different austenite content. (Geng, Sun, Guo, & Wang,
2015).
The resistance to prevent corrosion of AISI 2205 duplex stainless steel plates joined by Gas Metal
ArcWelding (GMAW) under the effect of electromagnetic interaction of low intensity (EMILI) was evaluated
with sensitive electrochemical methods. Weldings were made using two shielding gas mixtures: 98% Ar +
2%O2(M1) and 97% Ar + 3% N2(M2). Plates were welded under EMILI using the M1 gas with constant
welding parameters. The modified microstructural evolution in the high temperature HAZ and at the fusion area
induced by application of EMILI during welding is associated with the increase of resistance to localised
corrosion of the welded joints, which made by GMAW using the shielding gas M2 without the application of
Reducing Corrosion Rate by WeldingDesign
73
magnetic field presented high resistance to general corrosion. (García-Rentería, Morelos, Hernández, Pérez,
Ochoa, & Sánchez, 2014)
The above information, each step of process will affect the materials. In the welding process, corrosion
can be prevent with good design process. Welding process consist of some matters including groove weld
design and preheating. Groove weld design closely related with heat on the welding process. Pre-heating related
with stress on the steel. In this research, correlation between seam weld design, pre-heating and corrosion was
studied. Welding process will change some properties of steel. Good process design can be choosen to prevent
corrosion or reducing corrosion rate.
II. MATERIALS AND METHODE
A. Samples of experiment
In this tudy, ferritic malleable iron (SAE grade G 3500) with various groove weld design was used. The
composition of (wt%) of iron as follow Al 0,2% - Si 0,54% - K 0,29% - Ca 0,41 - Mn 1,02% - Fe 97,55%.
B. Pre heat welding treatment
The malleable iron heat at various temperature before welding. Temperature choosen was 400oC,
500oC, and 600oC. Holding time for pre heat was 30 minutes.
C. Welding process
SMAW (Shielded Metal Arc Welding) machine used to joint the samples. The filler metal used B 14
and RB 26 from kobe steel. In this study, groove design was V, 1/2V, X, and,. ½ X
Fig 1 : Groove welding design
In order to get the maximum quality of welding process, sertified welder was employed. The electric
current for welding process was about 80-130 ampere. The current adjusted based on the layer of welding
process. Mechanical and chemical properties of the filler metal described as follows:
Kobe Steel RB 26
C% Si% Mn% P% S%
0,008 0,30 0,37 0,012 0,010
YP (Mpa) TS (Mpa) El %
450 510 25
Kobe Steel B 14
C% Si% Mn% P% S%
0,10 0,10 0,43 0,015 0,007
YP (Mpa) TS (Mpa) El %
410 460 32
Reducing Corrosion Rate by Welding Design
74
D. Corrosion testing
For corrosion testing, special samples was prepared. Part of welded iron was cut on the HAZ area. The
dimension of Samples for corrosion testing is 5x5x25 mm. This testing use NaCl 5% solution.
III. RESULT AND DISCUSSION
A. Effect of Pre heating
Cooling rate on the welding process will make small temperature gradient at freezing process. Small
cooling rate will reduce formation of residual stress. On the high preheating temperature, cooling rate will be
reduced. So solidification processes also become slow. It causes the grain have enough time to grow, and
hardness of the material will be down.
Preheating on the welding process intends to reduce cooling rate on the heat affected zone. It means if
steel welded without preheat, cooling rate will be faster. Giving pre heat will reduce cooling rate, and also make
temperature uniform at heat affected zone so temperature gradient also become smaller.
B. Residual stress
Residual stress compressed stress or tensile stress without any external load from the outside, the
external load that is a force or temperature changes. Residual stress based on the size of stress on the grain.
Residual stress called macro stress if it entranced some grains. The other called micro stress if it residual stress
happened on the boundary or inside the grain. (wibowo, 2007)
This residual stress can be useful but it can also be useless. If the load tension and there is a residual
compressive stress in the material then the residual stress will give a negative resultant material to reduce the
effect of the load. Conversely, if there is a residual tensile stress in the material which has tensile load will
provide a positive resultante and if the resultant more than yield, it will begin the fracture.
C. Corrosion Rate
As explained before, type of groove weld and heating temperature could affect corrosion rate on steel.
For heating temperature 400 o
C, the graphic on table 1 explained the effect of welding groove type on corrosion
rate. Corrosion rate can be seen from lost of specimen weight.
Tabel 1: Weight of specimen vs days of corrosion test after preheating 400o
C
The graphic on tabel 1 showed that X welding joint has a highest corrosive resistant. After corrosion
test for 14 days, the material testing 0,57% lost. While ½ V welding groove is the worst in corrosion resistant,
because after 14 days corrosion test material testing 0,76 % lost.
Reducing Corrosion Rate by Welding Design
75
The samples with 5000
C preheating can be seen on tabel 2:
Tabel 2: Weight of specimen vs days of corrosion test after preheating 500oC
The graphic on tabel 2 showed that V welding joint has a highest corrosive resistant. After corrosion
test for 14 days, the material testing 0,51% lost . While ½ V welding groove is the worst in corrosion resistant,
because after 14 days corrosion test, material testing 0,61 % lost.
The samples with 6000
C preheating, can be seen on tabel 3:
Tabel 3: Weight of specimen vs days of corrosion test after preheating 600oC
The graphic on tabel 3 showed that X welding joint has a highest corrosive resistant. After corrosion
test for 14 days, the material testing 0,50% lost. While ½ V welding groove is the worst in corrosion resistant,
because after 14 days corrosion test material testing 0,69 % lost.
On the graphic tabel 1 , 2, and 3 by preheating on 500o
C and 600o
C give a better condition on
reducing corrosion rate, than after preheating 400o
C condition. For all welding groove type, material with 500o
C
and 600o
C preheating after 14 days corrosion test is 0,5%-0,69% lost. Material with 400o
C preheating after 14
days corrosion test is 0,57%-0,76% lost.
Reducing Corrosion Rate by Welding Design
76
Welding groove type also influence corrosion rate. X and V type welding groove show better condition
to reduce corrosion rate than ½ V and 1/2 X welding groove. After 14 days corrosion test, the material with X
welding groove is 0,5%-0,57% lost. The material with V welding groove after 14 days corrosion test is 0,51%-
0,59% lost.
After 14 days corrosion test, material with ½ X welding groove 0,58%-0,71% lost. Material with 1/2V
welding groove after 14 days corrosion test 0,61%-0,76% lost.
The different corrosion rate of samples can be caused by residual stress which happened after pre
heating and welding process. Preheating on 600o
C reduce cooling rate. X and V welding groove caused high
temperature on the materials, so the residual stress reduced.
Residual stress tested laboratory shows that some residual stress value can be explained below:
- Sample with C6 code (using X groove welding and 600o
C preheating) 1,7 Mpa
- Sample with E2 code (using ½ V groove welding and 400o
C preheating) 5,2 Mpa
Fig.3 shows corrosion on the sample. The corrosion is called pitting corrosion.
Fig.3: Pitting Corrosion
Pitting corrosion happened under certain conditions, especially at high concentrations of chlorides
(such as sodium chloride in sea water), high temperatures and exacerbated by low pH (i.e. acidic conditions).
(Kadry, 2008). Clorides attack the iron and high residual stress causes fast corrosion rate.
IV. CONCLUSION
The results obtained of this study can be summarized as follow:
a. Reducing corrosion rate can be solved by welding design process. The heat on the welding process must be
controlled.
b. Reducing corrosion rate by controlled residual stress on the welding process can be done by: pre heating 500-
600o
C for 30 minutes using X or V welding groove design
Reducing Corrosion Rate by Welding Design
77
REFFERENCES
[1]. García-Rentería, M., Morelos, V., Hernández, R. G., Pérez, L. D., Ochoa, G. E., & Sánchez, J. G.
(2014). Improvement of localised corrosion resistance of AISI 2205 Duplex Stainless Steel joints made
by gas metal arc welding under electromagnetic interaction of low intensity. Applied Surface Science,
252–260.
[2]. Geng, S., Sun, J., Guo, L., & Wang, H. (2015). Evolution of microstructure and corrosion behavior in
2205 duplex stainless steel GTA-welding joint. Journal of Manufacturing Processes, 32-37.
[3]. Kadry, S. (2008). Corrosion Analysis of Stainless Steel. European Journal of Scientific Research, 508-
516.
[4]. Mizhar, S., & Pandiangan, I. H. (2014). Effect of Heat Input To microstructure, hardness and
toughness In SMAW welding of 2.5 inch Diameter Steel Pipe. Jurnal Dinamis Vol.II,, 16-22.
[5]. Nikseresht, Z., Karimzadeh, F., Golozar, M., & Heidarbeigy, M. (2010). Effect of heat treatment on
microstructure and corrosion behavior of Al6061 alloy weldment. Materials and Design , 2643–2648.
[6]. Wibowo, a. (2007). Effect of Residual Stress of Frequency on Tones Bronze. Seminar Nasional
Teknologi 2007 (SNT 2007) (pp. B.2-.B5). Yogyakarta: UGM.
[7]. Xiong, J., Tan, M. Y., & Forsyth, M. (2013). The corrosion behaviors of stainless steel weldments in
sodium chloride solution observed using a novel electrochemical measurement approach. Desalination,
39-45.

Contenu connexe

Tendances

Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...
Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...
Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...IJERA Editor
 
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloy
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloyDry sliding wear behaviour of sand cast cu 11 ni-6sn alloy
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloyeSAT Publishing House
 
Development of grnn based tool for hardness measurement of homogeneous
Development of grnn based tool for hardness measurement of homogeneousDevelopment of grnn based tool for hardness measurement of homogeneous
Development of grnn based tool for hardness measurement of homogeneousIAEME Publication
 
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...Serviceability behavior of Reinforcement Concrete beams with polypropylene an...
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...IJERA Editor
 
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...IRJET Journal
 
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...IRJET Journal
 
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...IJERA Editor
 
Implementation of Generalized Regression Neural Network to Establish a Relati...
Implementation of Generalized Regression Neural Network to Establish a Relati...Implementation of Generalized Regression Neural Network to Establish a Relati...
Implementation of Generalized Regression Neural Network to Establish a Relati...IOSR Journals
 
The position of the joints with angle of 90° at friction stir welding (FSW)
The position of the joints with angle of 90° at friction stir welding (FSW)The position of the joints with angle of 90° at friction stir welding (FSW)
The position of the joints with angle of 90° at friction stir welding (FSW)UniversitasGadjahMada
 
IRJET - Performance of SFRC Beams under Combined State of Flexure, Direct...
IRJET -  	  Performance of SFRC Beams under Combined State of Flexure, Direct...IRJET -  	  Performance of SFRC Beams under Combined State of Flexure, Direct...
IRJET - Performance of SFRC Beams under Combined State of Flexure, Direct...IRJET Journal
 
Effect of prism height on strength of reinforced hollow concrete block masonry
Effect of prism height on strength of reinforced hollow concrete block masonryEffect of prism height on strength of reinforced hollow concrete block masonry
Effect of prism height on strength of reinforced hollow concrete block masonryeSAT Publishing House
 
Masonry beam deflection criteria5.doc
Masonry beam deflection criteria5.docMasonry beam deflection criteria5.doc
Masonry beam deflection criteria5.dochsaam hsaam
 
Study on Influence of heat treatment on Tribological properties of mild steel
Study on Influence of heat treatment on Tribological properties of mild steelStudy on Influence of heat treatment on Tribological properties of mild steel
Study on Influence of heat treatment on Tribological properties of mild steeldbpublications
 
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...IRJET Journal
 
Mechanical property assessment of austempered and conventionally hardened aisi
Mechanical property assessment of austempered and conventionally hardened aisiMechanical property assessment of austempered and conventionally hardened aisi
Mechanical property assessment of austempered and conventionally hardened aisiIAEME Publication
 

Tendances (19)

Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...
Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...
Investigation of Mechanical Properties of Aluminium Based Metal Matrix Compos...
 
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloy
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloyDry sliding wear behaviour of sand cast cu 11 ni-6sn alloy
Dry sliding wear behaviour of sand cast cu 11 ni-6sn alloy
 
Development of grnn based tool for hardness measurement of homogeneous
Development of grnn based tool for hardness measurement of homogeneousDevelopment of grnn based tool for hardness measurement of homogeneous
Development of grnn based tool for hardness measurement of homogeneous
 
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...Serviceability behavior of Reinforcement Concrete beams with polypropylene an...
Serviceability behavior of Reinforcement Concrete beams with polypropylene an...
 
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...
IRJET - Impact of Steel Fibers on the Hardened Properties of High Strength Co...
 
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...
IRJET - Experimental Study on the Influence of Reinforcement Corrosion on Fir...
 
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...
Effect of Coarse Aggregate Size on the Compressive Strength and the Flexural ...
 
Implementation of Generalized Regression Neural Network to Establish a Relati...
Implementation of Generalized Regression Neural Network to Establish a Relati...Implementation of Generalized Regression Neural Network to Establish a Relati...
Implementation of Generalized Regression Neural Network to Establish a Relati...
 
The position of the joints with angle of 90° at friction stir welding (FSW)
The position of the joints with angle of 90° at friction stir welding (FSW)The position of the joints with angle of 90° at friction stir welding (FSW)
The position of the joints with angle of 90° at friction stir welding (FSW)
 
IRJET - Performance of SFRC Beams under Combined State of Flexure, Direct...
IRJET -  	  Performance of SFRC Beams under Combined State of Flexure, Direct...IRJET -  	  Performance of SFRC Beams under Combined State of Flexure, Direct...
IRJET - Performance of SFRC Beams under Combined State of Flexure, Direct...
 
Dr.R.Narayanasamy - Super Plasticity
Dr.R.Narayanasamy - Super PlasticityDr.R.Narayanasamy - Super Plasticity
Dr.R.Narayanasamy - Super Plasticity
 
Effect of prism height on strength of reinforced hollow concrete block masonry
Effect of prism height on strength of reinforced hollow concrete block masonryEffect of prism height on strength of reinforced hollow concrete block masonry
Effect of prism height on strength of reinforced hollow concrete block masonry
 
Tiamte nr
Tiamte nrTiamte nr
Tiamte nr
 
Ijciet 06 10_016
Ijciet 06 10_016Ijciet 06 10_016
Ijciet 06 10_016
 
Masonry beam deflection criteria5.doc
Masonry beam deflection criteria5.docMasonry beam deflection criteria5.doc
Masonry beam deflection criteria5.doc
 
Study on Influence of heat treatment on Tribological properties of mild steel
Study on Influence of heat treatment on Tribological properties of mild steelStudy on Influence of heat treatment on Tribological properties of mild steel
Study on Influence of heat treatment on Tribological properties of mild steel
 
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...
Effect Of Tempering Process On Hydrogen Delayed Fracture Susceptibility Of 41...
 
30720130101006
3072013010100630720130101006
30720130101006
 
Mechanical property assessment of austempered and conventionally hardened aisi
Mechanical property assessment of austempered and conventionally hardened aisiMechanical property assessment of austempered and conventionally hardened aisi
Mechanical property assessment of austempered and conventionally hardened aisi
 

En vedette

A Novel Method for Prevention of Bandwidth Distributed Denial of Service Attacks
A Novel Method for Prevention of Bandwidth Distributed Denial of Service AttacksA Novel Method for Prevention of Bandwidth Distributed Denial of Service Attacks
A Novel Method for Prevention of Bandwidth Distributed Denial of Service AttacksIJERD Editor
 
Gold prospecting using Remote Sensing ‘A case study of Sudan’
Gold prospecting using Remote Sensing ‘A case study of Sudan’Gold prospecting using Remote Sensing ‘A case study of Sudan’
Gold prospecting using Remote Sensing ‘A case study of Sudan’IJERD Editor
 
Router 1X3 – RTL Design and Verification
Router 1X3 – RTL Design and VerificationRouter 1X3 – RTL Design and Verification
Router 1X3 – RTL Design and VerificationIJERD Editor
 
SMICO Aggregate Vibratory Screeners
SMICO Aggregate Vibratory ScreenersSMICO Aggregate Vibratory Screeners
SMICO Aggregate Vibratory ScreenersSMICO MFG
 
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...ijsrd.com
 
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...IJERD Editor
 
MEMS MICROPHONE INTERFACE
MEMS MICROPHONE INTERFACEMEMS MICROPHONE INTERFACE
MEMS MICROPHONE INTERFACEIJERD Editor
 
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVR
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVRMitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVR
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVRIJERD Editor
 
Vibrating feeder
Vibrating feederVibrating feeder
Vibrating feederJISHNU V
 
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...IJERD Editor
 
FEEDER & GRIZZLY STEEL STRUCTRE
FEEDER & GRIZZLY STEEL STRUCTREFEEDER & GRIZZLY STEEL STRUCTRE
FEEDER & GRIZZLY STEEL STRUCTRETokunbo Akinsara
 

En vedette (15)

A Novel Method for Prevention of Bandwidth Distributed Denial of Service Attacks
A Novel Method for Prevention of Bandwidth Distributed Denial of Service AttacksA Novel Method for Prevention of Bandwidth Distributed Denial of Service Attacks
A Novel Method for Prevention of Bandwidth Distributed Denial of Service Attacks
 
Gold prospecting using Remote Sensing ‘A case study of Sudan’
Gold prospecting using Remote Sensing ‘A case study of Sudan’Gold prospecting using Remote Sensing ‘A case study of Sudan’
Gold prospecting using Remote Sensing ‘A case study of Sudan’
 
www.ijerd.com
www.ijerd.comwww.ijerd.com
www.ijerd.com
 
www.ijerd.com
www.ijerd.comwww.ijerd.com
www.ijerd.com
 
Properl
ProperlProperl
Properl
 
Vibrating feeder
Vibrating feederVibrating feeder
Vibrating feeder
 
Router 1X3 – RTL Design and Verification
Router 1X3 – RTL Design and VerificationRouter 1X3 – RTL Design and Verification
Router 1X3 – RTL Design and Verification
 
SMICO Aggregate Vibratory Screeners
SMICO Aggregate Vibratory ScreenersSMICO Aggregate Vibratory Screeners
SMICO Aggregate Vibratory Screeners
 
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...
Design Modification of Failure Mode Effect Analysis of Vibrating Feeder used ...
 
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...
Active Power Exchange in Distributed Power-Flow Controller (DPFC) At Third Ha...
 
MEMS MICROPHONE INTERFACE
MEMS MICROPHONE INTERFACEMEMS MICROPHONE INTERFACE
MEMS MICROPHONE INTERFACE
 
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVR
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVRMitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVR
Mitigation of Voltage Sag/Swell with Fuzzy Control Reduced Rating DVR
 
Vibrating feeder
Vibrating feederVibrating feeder
Vibrating feeder
 
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...
Fly Ash as a Partial Replacement of Cement in Concrete and Durability Study o...
 
FEEDER & GRIZZLY STEEL STRUCTRE
FEEDER & GRIZZLY STEEL STRUCTREFEEDER & GRIZZLY STEEL STRUCTRE
FEEDER & GRIZZLY STEEL STRUCTRE
 

Similaire à Reducing Corrosion Rate by Welding Design

REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...
REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...
REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...ijiert bestjournal
 
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...IRJET Journal
 
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blanking
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blankingVacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blanking
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blankingEVP Vacuum pump
 
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...Dr. Amarjeet Singh
 
An assessment of the microstraft
An assessment of the microstraftAn assessment of the microstraft
An assessment of the microstraftAlexander Decker
 
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...IJMER
 
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304L
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304LEvaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304L
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304LIRJET Journal
 
Study of effects of heat treatment on the hardness and microstructure of weld...
Study of effects of heat treatment on the hardness and microstructure of weld...Study of effects of heat treatment on the hardness and microstructure of weld...
Study of effects of heat treatment on the hardness and microstructure of weld...Alexander Decker
 
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...IJMER
 
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...IJAEMSJORNAL
 
1 s2.0-s2214785319313859-main
1 s2.0-s2214785319313859-main1 s2.0-s2214785319313859-main
1 s2.0-s2214785319313859-mainPRAWEEN KUMAR
 
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...Journal For Research
 
Analysis and Improvement of Distortion of Lathe Machine Main Spindle
Analysis and Improvement of Distortion of Lathe Machine Main SpindleAnalysis and Improvement of Distortion of Lathe Machine Main Spindle
Analysis and Improvement of Distortion of Lathe Machine Main SpindleIRJET Journal
 
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803IRJET Journal
 
IRJET - Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...
IRJET -  	  Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...IRJET -  	  Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...
IRJET - Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...IRJET Journal
 
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...ijsrd.com
 

Similaire à Reducing Corrosion Rate by Welding Design (20)

REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...
REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...
REVIEW ON EFFECT OF HEAT INPUT ON TENSILE STRENGTH OF BUTT WELD JOINT USING M...
 
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...
IRJET- Investigation on Dissimilar Metal Welding of Stainless Steel 316 L and...
 
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blanking
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blankingVacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blanking
Vacuum furnace simuwu_improved_vacuum_heat-treatment_for_fine-blanking
 
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...
Optimization on Spot Weld Parameters in Resistance Spot Welding Process on AI...
 
An assessment of the microstraft
An assessment of the microstraftAn assessment of the microstraft
An assessment of the microstraft
 
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...
Study on Effect of Manual Metal Arc Welding Process Parameters on Width of He...
 
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304L
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304LEvaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304L
Evaluation of Hardness of Bimetallic Weld joint between SA-508Gr3 and SS-304L
 
Study of effects of heat treatment on the hardness and microstructure of weld...
Study of effects of heat treatment on the hardness and microstructure of weld...Study of effects of heat treatment on the hardness and microstructure of weld...
Study of effects of heat treatment on the hardness and microstructure of weld...
 
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...
Effects of Continuous Cooling On Impact and Micro Structural Properties of Lo...
 
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...
Comparison of Mechanical Properties of Austempered, Normalized and As-Weld Ca...
 
1 s2.0-s2214785319313859-main
1 s2.0-s2214785319313859-main1 s2.0-s2214785319313859-main
1 s2.0-s2214785319313859-main
 
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...
INVESTIGATION OF RESIDUAL STRESSES IN WELDING AND ITS EFFECT ON MECHANICAL BE...
 
EFFECTS OF QUENCHANTS ON IMPACT STRENGTH OF SINGLE-VEE BUTT WELDED JOINT OF M...
EFFECTS OF QUENCHANTS ON IMPACT STRENGTH OF SINGLE-VEE BUTT WELDED JOINT OF M...EFFECTS OF QUENCHANTS ON IMPACT STRENGTH OF SINGLE-VEE BUTT WELDED JOINT OF M...
EFFECTS OF QUENCHANTS ON IMPACT STRENGTH OF SINGLE-VEE BUTT WELDED JOINT OF M...
 
Analysis and Improvement of Distortion of Lathe Machine Main Spindle
Analysis and Improvement of Distortion of Lathe Machine Main SpindleAnalysis and Improvement of Distortion of Lathe Machine Main Spindle
Analysis and Improvement of Distortion of Lathe Machine Main Spindle
 
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803
IRJET- Optimization on Friction Welding of Duplex Stainless Steel-S31803
 
Oz3426202627
Oz3426202627Oz3426202627
Oz3426202627
 
IRJET - Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...
IRJET -  	  Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...IRJET -  	  Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...
IRJET - Dissimilar Welding of Alloy Steel and Stainless Steel by using Va...
 
Ijmet 10 01_004
Ijmet 10 01_004Ijmet 10 01_004
Ijmet 10 01_004
 
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...
Modeling and Simulation of Base Plate of Friction Stir Welding-Advanced Weldi...
 
FSW.pdf
FSW.pdfFSW.pdf
FSW.pdf
 

Plus de IJERD Editor

Study on the Fused Deposition Modelling In Additive Manufacturing
Study on the Fused Deposition Modelling In Additive ManufacturingStudy on the Fused Deposition Modelling In Additive Manufacturing
Study on the Fused Deposition Modelling In Additive ManufacturingIJERD Editor
 
Spyware triggering system by particular string value
Spyware triggering system by particular string valueSpyware triggering system by particular string value
Spyware triggering system by particular string valueIJERD Editor
 
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...IJERD Editor
 
Secure Image Transmission for Cloud Storage System Using Hybrid Scheme
Secure Image Transmission for Cloud Storage System Using Hybrid SchemeSecure Image Transmission for Cloud Storage System Using Hybrid Scheme
Secure Image Transmission for Cloud Storage System Using Hybrid SchemeIJERD Editor
 
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...IJERD Editor
 
Gesture Gaming on the World Wide Web Using an Ordinary Web Camera
Gesture Gaming on the World Wide Web Using an Ordinary Web CameraGesture Gaming on the World Wide Web Using an Ordinary Web Camera
Gesture Gaming on the World Wide Web Using an Ordinary Web CameraIJERD Editor
 
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...IJERD Editor
 
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...IJERD Editor
 
Moon-bounce: A Boon for VHF Dxing
Moon-bounce: A Boon for VHF DxingMoon-bounce: A Boon for VHF Dxing
Moon-bounce: A Boon for VHF DxingIJERD Editor
 
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...IJERD Editor
 
Importance of Measurements in Smart Grid
Importance of Measurements in Smart GridImportance of Measurements in Smart Grid
Importance of Measurements in Smart GridIJERD Editor
 
Study of Macro level Properties of SCC using GGBS and Lime stone powder
Study of Macro level Properties of SCC using GGBS and Lime stone powderStudy of Macro level Properties of SCC using GGBS and Lime stone powder
Study of Macro level Properties of SCC using GGBS and Lime stone powderIJERD Editor
 
Seismic Drift Consideration in soft storied RCC buildings: A Critical Review
Seismic Drift Consideration in soft storied RCC buildings: A Critical ReviewSeismic Drift Consideration in soft storied RCC buildings: A Critical Review
Seismic Drift Consideration in soft storied RCC buildings: A Critical ReviewIJERD Editor
 
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standards
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standardsPost processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standards
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standardsIJERD Editor
 
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...IJERD Editor
 
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...Content Based Video Retrieval Using Integrated Feature Extraction and Persona...
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...IJERD Editor
 
Planar Internal Antenna Design for Cellular Applications & SAR Analysis
Planar Internal Antenna Design for Cellular Applications & SAR AnalysisPlanar Internal Antenna Design for Cellular Applications & SAR Analysis
Planar Internal Antenna Design for Cellular Applications & SAR AnalysisIJERD Editor
 
Intelligent learning management system starters
Intelligent learning management system startersIntelligent learning management system starters
Intelligent learning management system startersIJERD Editor
 
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) technique
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) techniqueJoint State and Parameter Estimation by Extended Kalman Filter (EKF) technique
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) techniqueIJERD Editor
 
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...Experimental Study of Material Removal Efficiency in EDM Using Various Types ...
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...IJERD Editor
 

Plus de IJERD Editor (20)

Study on the Fused Deposition Modelling In Additive Manufacturing
Study on the Fused Deposition Modelling In Additive ManufacturingStudy on the Fused Deposition Modelling In Additive Manufacturing
Study on the Fused Deposition Modelling In Additive Manufacturing
 
Spyware triggering system by particular string value
Spyware triggering system by particular string valueSpyware triggering system by particular string value
Spyware triggering system by particular string value
 
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...
A Blind Steganalysis on JPEG Gray Level Image Based on Statistical Features a...
 
Secure Image Transmission for Cloud Storage System Using Hybrid Scheme
Secure Image Transmission for Cloud Storage System Using Hybrid SchemeSecure Image Transmission for Cloud Storage System Using Hybrid Scheme
Secure Image Transmission for Cloud Storage System Using Hybrid Scheme
 
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...
Application of Buckley-Leverett Equation in Modeling the Radius of Invasion i...
 
Gesture Gaming on the World Wide Web Using an Ordinary Web Camera
Gesture Gaming on the World Wide Web Using an Ordinary Web CameraGesture Gaming on the World Wide Web Using an Ordinary Web Camera
Gesture Gaming on the World Wide Web Using an Ordinary Web Camera
 
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...
Hardware Analysis of Resonant Frequency Converter Using Isolated Circuits And...
 
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...
Simulated Analysis of Resonant Frequency Converter Using Different Tank Circu...
 
Moon-bounce: A Boon for VHF Dxing
Moon-bounce: A Boon for VHF DxingMoon-bounce: A Boon for VHF Dxing
Moon-bounce: A Boon for VHF Dxing
 
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...
“MS-Extractor: An Innovative Approach to Extract Microsatellites on „Y‟ Chrom...
 
Importance of Measurements in Smart Grid
Importance of Measurements in Smart GridImportance of Measurements in Smart Grid
Importance of Measurements in Smart Grid
 
Study of Macro level Properties of SCC using GGBS and Lime stone powder
Study of Macro level Properties of SCC using GGBS and Lime stone powderStudy of Macro level Properties of SCC using GGBS and Lime stone powder
Study of Macro level Properties of SCC using GGBS and Lime stone powder
 
Seismic Drift Consideration in soft storied RCC buildings: A Critical Review
Seismic Drift Consideration in soft storied RCC buildings: A Critical ReviewSeismic Drift Consideration in soft storied RCC buildings: A Critical Review
Seismic Drift Consideration in soft storied RCC buildings: A Critical Review
 
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standards
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standardsPost processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standards
Post processing of SLM Ti-6Al-4V Alloy in accordance with AMS 4928 standards
 
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...
Treatment of Waste Water from Organic Fraction Incineration of Municipal Soli...
 
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...Content Based Video Retrieval Using Integrated Feature Extraction and Persona...
Content Based Video Retrieval Using Integrated Feature Extraction and Persona...
 
Planar Internal Antenna Design for Cellular Applications & SAR Analysis
Planar Internal Antenna Design for Cellular Applications & SAR AnalysisPlanar Internal Antenna Design for Cellular Applications & SAR Analysis
Planar Internal Antenna Design for Cellular Applications & SAR Analysis
 
Intelligent learning management system starters
Intelligent learning management system startersIntelligent learning management system starters
Intelligent learning management system starters
 
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) technique
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) techniqueJoint State and Parameter Estimation by Extended Kalman Filter (EKF) technique
Joint State and Parameter Estimation by Extended Kalman Filter (EKF) technique
 
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...Experimental Study of Material Removal Efficiency in EDM Using Various Types ...
Experimental Study of Material Removal Efficiency in EDM Using Various Types ...
 

Dernier

Introduction to Matsuo Laboratory (ENG).pptx
Introduction to Matsuo Laboratory (ENG).pptxIntroduction to Matsuo Laboratory (ENG).pptx
Introduction to Matsuo Laboratory (ENG).pptxMatsuo Lab
 
NIST Cybersecurity Framework (CSF) 2.0 Workshop
NIST Cybersecurity Framework (CSF) 2.0 WorkshopNIST Cybersecurity Framework (CSF) 2.0 Workshop
NIST Cybersecurity Framework (CSF) 2.0 WorkshopBachir Benyammi
 
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdf
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdfIaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdf
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdfDaniel Santiago Silva Capera
 
Cybersecurity Workshop #1.pptx
Cybersecurity Workshop #1.pptxCybersecurity Workshop #1.pptx
Cybersecurity Workshop #1.pptxGDSC PJATK
 
UiPath Community: AI for UiPath Automation Developers
UiPath Community: AI for UiPath Automation DevelopersUiPath Community: AI for UiPath Automation Developers
UiPath Community: AI for UiPath Automation DevelopersUiPathCommunity
 
How Accurate are Carbon Emissions Projections?
How Accurate are Carbon Emissions Projections?How Accurate are Carbon Emissions Projections?
How Accurate are Carbon Emissions Projections?IES VE
 
AI Fame Rush Review – Virtual Influencer Creation In Just Minutes
AI Fame Rush Review – Virtual Influencer Creation In Just MinutesAI Fame Rush Review – Virtual Influencer Creation In Just Minutes
AI Fame Rush Review – Virtual Influencer Creation In Just MinutesMd Hossain Ali
 
Designing A Time bound resource download URL
Designing A Time bound resource download URLDesigning A Time bound resource download URL
Designing A Time bound resource download URLRuncy Oommen
 
Building Your Own AI Instance (TBLC AI )
Building Your Own AI Instance (TBLC AI )Building Your Own AI Instance (TBLC AI )
Building Your Own AI Instance (TBLC AI )Brian Pichman
 
COMPUTER 10 Lesson 8 - Building a Website
COMPUTER 10 Lesson 8 - Building a WebsiteCOMPUTER 10 Lesson 8 - Building a Website
COMPUTER 10 Lesson 8 - Building a Websitedgelyza
 
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019IES VE
 
Building AI-Driven Apps Using Semantic Kernel.pptx
Building AI-Driven Apps Using Semantic Kernel.pptxBuilding AI-Driven Apps Using Semantic Kernel.pptx
Building AI-Driven Apps Using Semantic Kernel.pptxUdaiappa Ramachandran
 
UiPath Platform: The Backend Engine Powering Your Automation - Session 1
UiPath Platform: The Backend Engine Powering Your Automation - Session 1UiPath Platform: The Backend Engine Powering Your Automation - Session 1
UiPath Platform: The Backend Engine Powering Your Automation - Session 1DianaGray10
 
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdf
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdf
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdfJamie (Taka) Wang
 
Basic Building Blocks of Internet of Things.
Basic Building Blocks of Internet of Things.Basic Building Blocks of Internet of Things.
Basic Building Blocks of Internet of Things.YounusS2
 
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDE
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDEADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDE
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDELiveplex
 
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve Decarbonization
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve DecarbonizationUsing IESVE for Loads, Sizing and Heat Pump Modeling to Achieve Decarbonization
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve DecarbonizationIES VE
 
COMPUTER 10: Lesson 7 - File Storage and Online Collaboration
COMPUTER 10: Lesson 7 - File Storage and Online CollaborationCOMPUTER 10: Lesson 7 - File Storage and Online Collaboration
COMPUTER 10: Lesson 7 - File Storage and Online Collaborationbruanjhuli
 
Empowering Africa's Next Generation: The AI Leadership Blueprint
Empowering Africa's Next Generation: The AI Leadership BlueprintEmpowering Africa's Next Generation: The AI Leadership Blueprint
Empowering Africa's Next Generation: The AI Leadership BlueprintMahmoud Rabie
 

Dernier (20)

Introduction to Matsuo Laboratory (ENG).pptx
Introduction to Matsuo Laboratory (ENG).pptxIntroduction to Matsuo Laboratory (ENG).pptx
Introduction to Matsuo Laboratory (ENG).pptx
 
NIST Cybersecurity Framework (CSF) 2.0 Workshop
NIST Cybersecurity Framework (CSF) 2.0 WorkshopNIST Cybersecurity Framework (CSF) 2.0 Workshop
NIST Cybersecurity Framework (CSF) 2.0 Workshop
 
20230104 - machine vision
20230104 - machine vision20230104 - machine vision
20230104 - machine vision
 
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdf
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdfIaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdf
IaC & GitOps in a Nutshell - a FridayInANuthshell Episode.pdf
 
Cybersecurity Workshop #1.pptx
Cybersecurity Workshop #1.pptxCybersecurity Workshop #1.pptx
Cybersecurity Workshop #1.pptx
 
UiPath Community: AI for UiPath Automation Developers
UiPath Community: AI for UiPath Automation DevelopersUiPath Community: AI for UiPath Automation Developers
UiPath Community: AI for UiPath Automation Developers
 
How Accurate are Carbon Emissions Projections?
How Accurate are Carbon Emissions Projections?How Accurate are Carbon Emissions Projections?
How Accurate are Carbon Emissions Projections?
 
AI Fame Rush Review – Virtual Influencer Creation In Just Minutes
AI Fame Rush Review – Virtual Influencer Creation In Just MinutesAI Fame Rush Review – Virtual Influencer Creation In Just Minutes
AI Fame Rush Review – Virtual Influencer Creation In Just Minutes
 
Designing A Time bound resource download URL
Designing A Time bound resource download URLDesigning A Time bound resource download URL
Designing A Time bound resource download URL
 
Building Your Own AI Instance (TBLC AI )
Building Your Own AI Instance (TBLC AI )Building Your Own AI Instance (TBLC AI )
Building Your Own AI Instance (TBLC AI )
 
COMPUTER 10 Lesson 8 - Building a Website
COMPUTER 10 Lesson 8 - Building a WebsiteCOMPUTER 10 Lesson 8 - Building a Website
COMPUTER 10 Lesson 8 - Building a Website
 
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019
IESVE Software for Florida Code Compliance Using ASHRAE 90.1-2019
 
Building AI-Driven Apps Using Semantic Kernel.pptx
Building AI-Driven Apps Using Semantic Kernel.pptxBuilding AI-Driven Apps Using Semantic Kernel.pptx
Building AI-Driven Apps Using Semantic Kernel.pptx
 
UiPath Platform: The Backend Engine Powering Your Automation - Session 1
UiPath Platform: The Backend Engine Powering Your Automation - Session 1UiPath Platform: The Backend Engine Powering Your Automation - Session 1
UiPath Platform: The Backend Engine Powering Your Automation - Session 1
 
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdf
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdf
activity_diagram_combine_v4_20190827.pdfactivity_diagram_combine_v4_20190827.pdf
 
Basic Building Blocks of Internet of Things.
Basic Building Blocks of Internet of Things.Basic Building Blocks of Internet of Things.
Basic Building Blocks of Internet of Things.
 
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDE
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDEADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDE
ADOPTING WEB 3 FOR YOUR BUSINESS: A STEP-BY-STEP GUIDE
 
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve Decarbonization
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve DecarbonizationUsing IESVE for Loads, Sizing and Heat Pump Modeling to Achieve Decarbonization
Using IESVE for Loads, Sizing and Heat Pump Modeling to Achieve Decarbonization
 
COMPUTER 10: Lesson 7 - File Storage and Online Collaboration
COMPUTER 10: Lesson 7 - File Storage and Online CollaborationCOMPUTER 10: Lesson 7 - File Storage and Online Collaboration
COMPUTER 10: Lesson 7 - File Storage and Online Collaboration
 
Empowering Africa's Next Generation: The AI Leadership Blueprint
Empowering Africa's Next Generation: The AI Leadership BlueprintEmpowering Africa's Next Generation: The AI Leadership Blueprint
Empowering Africa's Next Generation: The AI Leadership Blueprint
 

Reducing Corrosion Rate by Welding Design

  • 1. International Journal of Engineering Research and Development e-ISSN: 2278-067X, p-ISSN: 2278-800X, www.ijerd.com Volume 11, Issue 09 (September 2015), PP.72-77 72 Reducing Corrosion Rate by Welding Design Muhammad Akhlis Rizza 1 , Anang Takwanto 2 1 Mechanical Engineering Dept, State Polytechnic of Malang, Jl. Soekarno Hatta 9 Malang, Indonesia. 2 Chemichal Engineering Dept, ,State Polytechnic of Malang, Jl. Soekarno Hatta 9 Malang, Indonesia. Abstract:- The paper addresses the importance of welding design to prevent corrosion at steel. Welding is used to join pipe, profiles at bridges, spindle, and a lot more part of engineering construction. The problems happened associated with welding are common issues in these fields, especially corrosion. Corrosion can be reduced with many methods, they are painting, controlling humidity, and also good welding design. In the research, it can be found that reducing residual stress on the welding can be solved in corrosion rate reduction problem. Preheating on 500oC and 600oC give better condition to reduce corosion rate than condition after preheating 400oC. For all welding groove type, material with 500oC and 600oC preheating after 14 days corrosion test is 0,5%-0,69% lost. Material with 400oC preheating after 14 days corrosion test is 0,57%-0,76% lost. Welding groove also influence corrosion rate. X and V type welding groove give better condition to reduce corrosion rate than use 1/2V and 1/2 X welding groove. After 14 days corrosion test, the samples with X welding groove type is 0,5%-0,57% lost. The samples with V welding groove after 14 days corrosion test is 0,51%-0,59% lost. The samples with 1/2V and 1/2X welding groove after 14 days corrosion test is 0,58%- 0,71% lost. Keywords:- welding, corrosion, pre-heating, residual stress. I. INTRODUCTION Corrosion is depravation of essential properties in a material due to reactions with its environment. Millions of dollars are lost each year because of corrosion. Much of this loss is due to the corrosion of iron and steel, although many other metals may corrode as well. (Kadry, 2008). Welding process can make some changes of microstructures, formation of residual stresses due to the non-uniform temperature distribution during the welding thermal cycle. The changes in microstructures and surface conditions are non-uniform. Each different zone of a weldment is expected to have different corrosion behavior. (Xiong, Tan, & Forsyth, 2013) Welding process become very important since almost all of joint in engineering system using various kind of welding process. Researcher tries to solve side effect of welding process, including corrosion. The corrosion behaviour and microstructure of Al6061 alloy welded by GTAW (Gas tungsten arc welding) and followed by various heat treatments have been researched. The microstructure of both weld metal (WM) and base metal (BM) was investigated using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Corrosion behavior was investigated in 3.5 wt.% NaCl aqueous solution. The results showed that BM consists of Fe-rich coarse intermetallic particles. (Nikseresht, Karimzadeh, Golozar, & Heidarbeigy, 2010) Some mechanical properties and corrosion behavior in five zones from the weld metal to base metal of a 2205 duplex stainless steel joint, which was welded by double-pass tungsten inert gas arc welding with filler wire was investigated. Results of the research showed that a great deal of secondary austenite appeared in weld metal due to the reheat of second pass welding and coarse ferrite grains were formed near the fusion line, while other zones had the similar microstructures with a different austenite content. (Geng, Sun, Guo, & Wang, 2015). The resistance to prevent corrosion of AISI 2205 duplex stainless steel plates joined by Gas Metal ArcWelding (GMAW) under the effect of electromagnetic interaction of low intensity (EMILI) was evaluated with sensitive electrochemical methods. Weldings were made using two shielding gas mixtures: 98% Ar + 2%O2(M1) and 97% Ar + 3% N2(M2). Plates were welded under EMILI using the M1 gas with constant welding parameters. The modified microstructural evolution in the high temperature HAZ and at the fusion area induced by application of EMILI during welding is associated with the increase of resistance to localised corrosion of the welded joints, which made by GMAW using the shielding gas M2 without the application of
  • 2. Reducing Corrosion Rate by WeldingDesign 73 magnetic field presented high resistance to general corrosion. (García-Rentería, Morelos, Hernández, Pérez, Ochoa, & Sánchez, 2014) The above information, each step of process will affect the materials. In the welding process, corrosion can be prevent with good design process. Welding process consist of some matters including groove weld design and preheating. Groove weld design closely related with heat on the welding process. Pre-heating related with stress on the steel. In this research, correlation between seam weld design, pre-heating and corrosion was studied. Welding process will change some properties of steel. Good process design can be choosen to prevent corrosion or reducing corrosion rate. II. MATERIALS AND METHODE A. Samples of experiment In this tudy, ferritic malleable iron (SAE grade G 3500) with various groove weld design was used. The composition of (wt%) of iron as follow Al 0,2% - Si 0,54% - K 0,29% - Ca 0,41 - Mn 1,02% - Fe 97,55%. B. Pre heat welding treatment The malleable iron heat at various temperature before welding. Temperature choosen was 400oC, 500oC, and 600oC. Holding time for pre heat was 30 minutes. C. Welding process SMAW (Shielded Metal Arc Welding) machine used to joint the samples. The filler metal used B 14 and RB 26 from kobe steel. In this study, groove design was V, 1/2V, X, and,. ½ X Fig 1 : Groove welding design In order to get the maximum quality of welding process, sertified welder was employed. The electric current for welding process was about 80-130 ampere. The current adjusted based on the layer of welding process. Mechanical and chemical properties of the filler metal described as follows: Kobe Steel RB 26 C% Si% Mn% P% S% 0,008 0,30 0,37 0,012 0,010 YP (Mpa) TS (Mpa) El % 450 510 25 Kobe Steel B 14 C% Si% Mn% P% S% 0,10 0,10 0,43 0,015 0,007 YP (Mpa) TS (Mpa) El % 410 460 32
  • 3. Reducing Corrosion Rate by Welding Design 74 D. Corrosion testing For corrosion testing, special samples was prepared. Part of welded iron was cut on the HAZ area. The dimension of Samples for corrosion testing is 5x5x25 mm. This testing use NaCl 5% solution. III. RESULT AND DISCUSSION A. Effect of Pre heating Cooling rate on the welding process will make small temperature gradient at freezing process. Small cooling rate will reduce formation of residual stress. On the high preheating temperature, cooling rate will be reduced. So solidification processes also become slow. It causes the grain have enough time to grow, and hardness of the material will be down. Preheating on the welding process intends to reduce cooling rate on the heat affected zone. It means if steel welded without preheat, cooling rate will be faster. Giving pre heat will reduce cooling rate, and also make temperature uniform at heat affected zone so temperature gradient also become smaller. B. Residual stress Residual stress compressed stress or tensile stress without any external load from the outside, the external load that is a force or temperature changes. Residual stress based on the size of stress on the grain. Residual stress called macro stress if it entranced some grains. The other called micro stress if it residual stress happened on the boundary or inside the grain. (wibowo, 2007) This residual stress can be useful but it can also be useless. If the load tension and there is a residual compressive stress in the material then the residual stress will give a negative resultant material to reduce the effect of the load. Conversely, if there is a residual tensile stress in the material which has tensile load will provide a positive resultante and if the resultant more than yield, it will begin the fracture. C. Corrosion Rate As explained before, type of groove weld and heating temperature could affect corrosion rate on steel. For heating temperature 400 o C, the graphic on table 1 explained the effect of welding groove type on corrosion rate. Corrosion rate can be seen from lost of specimen weight. Tabel 1: Weight of specimen vs days of corrosion test after preheating 400o C The graphic on tabel 1 showed that X welding joint has a highest corrosive resistant. After corrosion test for 14 days, the material testing 0,57% lost. While ½ V welding groove is the worst in corrosion resistant, because after 14 days corrosion test material testing 0,76 % lost.
  • 4. Reducing Corrosion Rate by Welding Design 75 The samples with 5000 C preheating can be seen on tabel 2: Tabel 2: Weight of specimen vs days of corrosion test after preheating 500oC The graphic on tabel 2 showed that V welding joint has a highest corrosive resistant. After corrosion test for 14 days, the material testing 0,51% lost . While ½ V welding groove is the worst in corrosion resistant, because after 14 days corrosion test, material testing 0,61 % lost. The samples with 6000 C preheating, can be seen on tabel 3: Tabel 3: Weight of specimen vs days of corrosion test after preheating 600oC The graphic on tabel 3 showed that X welding joint has a highest corrosive resistant. After corrosion test for 14 days, the material testing 0,50% lost. While ½ V welding groove is the worst in corrosion resistant, because after 14 days corrosion test material testing 0,69 % lost. On the graphic tabel 1 , 2, and 3 by preheating on 500o C and 600o C give a better condition on reducing corrosion rate, than after preheating 400o C condition. For all welding groove type, material with 500o C and 600o C preheating after 14 days corrosion test is 0,5%-0,69% lost. Material with 400o C preheating after 14 days corrosion test is 0,57%-0,76% lost.
  • 5. Reducing Corrosion Rate by Welding Design 76 Welding groove type also influence corrosion rate. X and V type welding groove show better condition to reduce corrosion rate than ½ V and 1/2 X welding groove. After 14 days corrosion test, the material with X welding groove is 0,5%-0,57% lost. The material with V welding groove after 14 days corrosion test is 0,51%- 0,59% lost. After 14 days corrosion test, material with ½ X welding groove 0,58%-0,71% lost. Material with 1/2V welding groove after 14 days corrosion test 0,61%-0,76% lost. The different corrosion rate of samples can be caused by residual stress which happened after pre heating and welding process. Preheating on 600o C reduce cooling rate. X and V welding groove caused high temperature on the materials, so the residual stress reduced. Residual stress tested laboratory shows that some residual stress value can be explained below: - Sample with C6 code (using X groove welding and 600o C preheating) 1,7 Mpa - Sample with E2 code (using ½ V groove welding and 400o C preheating) 5,2 Mpa Fig.3 shows corrosion on the sample. The corrosion is called pitting corrosion. Fig.3: Pitting Corrosion Pitting corrosion happened under certain conditions, especially at high concentrations of chlorides (such as sodium chloride in sea water), high temperatures and exacerbated by low pH (i.e. acidic conditions). (Kadry, 2008). Clorides attack the iron and high residual stress causes fast corrosion rate. IV. CONCLUSION The results obtained of this study can be summarized as follow: a. Reducing corrosion rate can be solved by welding design process. The heat on the welding process must be controlled. b. Reducing corrosion rate by controlled residual stress on the welding process can be done by: pre heating 500- 600o C for 30 minutes using X or V welding groove design
  • 6. Reducing Corrosion Rate by Welding Design 77 REFFERENCES [1]. García-Rentería, M., Morelos, V., Hernández, R. G., Pérez, L. D., Ochoa, G. E., & Sánchez, J. G. (2014). Improvement of localised corrosion resistance of AISI 2205 Duplex Stainless Steel joints made by gas metal arc welding under electromagnetic interaction of low intensity. Applied Surface Science, 252–260. [2]. Geng, S., Sun, J., Guo, L., & Wang, H. (2015). Evolution of microstructure and corrosion behavior in 2205 duplex stainless steel GTA-welding joint. Journal of Manufacturing Processes, 32-37. [3]. Kadry, S. (2008). Corrosion Analysis of Stainless Steel. European Journal of Scientific Research, 508- 516. [4]. Mizhar, S., & Pandiangan, I. H. (2014). Effect of Heat Input To microstructure, hardness and toughness In SMAW welding of 2.5 inch Diameter Steel Pipe. Jurnal Dinamis Vol.II,, 16-22. [5]. Nikseresht, Z., Karimzadeh, F., Golozar, M., & Heidarbeigy, M. (2010). Effect of heat treatment on microstructure and corrosion behavior of Al6061 alloy weldment. Materials and Design , 2643–2648. [6]. Wibowo, a. (2007). Effect of Residual Stress of Frequency on Tones Bronze. Seminar Nasional Teknologi 2007 (SNT 2007) (pp. B.2-.B5). Yogyakarta: UGM. [7]. Xiong, J., Tan, M. Y., & Forsyth, M. (2013). The corrosion behaviors of stainless steel weldments in sodium chloride solution observed using a novel electrochemical measurement approach. Desalination, 39-45.