Aurélie Mossé, Designer-chercheur et Enseignante I PhD I MA Design for Textile Futures I www.aureliemosse.com I info@aurelimosse.com

1. Stéréolux, Nantes, 27 mai 2015
«Les matières textiles du futur»: table ronde
Aurélie Mossé l Designer-chercheur et Enseignante l PhD l MA Design for Textile Futures l www.aureliemosse.com l info@aureliemosse.com

2. Gossamer Timescapes:
Designing Self-actuated Textiles
for the Home PhD Thesis by Aurélie Mossé
The Royal Danish Academy of Fine Arts,
Schools of Architecture, Design and Conservation
Centre for IT & Architecture,
Copenhagen, Denmark
The Royal Danish Academy of Fine Arts,
Schools of Architecture, Design and Conservation
School of Architecture
Recherche - textiles actifs pour l’environnement maison
Explorer par le design le potentiel culturel/poétique des technologies intelligentes et leur contribution à la construction d’une maison plus durable
Programming materials at molecular level
Light-responsive polymer films by Ele de Boer, TU Eindhoven
Plastiques lumino-actifs Plastiques électro-actifs

3. Textiles «intelligents»
Matériaux textiles avec la capacité de sentir une information et d’y répondre avec un comportement spécifique
1/ matériaux qui brouillent la frontière entre idée de matériau (statique) et
machine (dynamique)
2/ matériaux qui introduisent le temps comme dimen-
sion centrale de la création
Reef, Aurélie Mossé, 2011

4. Générer de l’électricité
Les technologies photovoltaiques
The Photovoltaic Mashrabiya, Aurélie Mossé, 2009

5. Changement de forme
Exemple des polymères électro-actifs
Reef, Aurélie Mossé, 2011, in collaboration with Guggi Kofod, Potsdam University & David Gauthier, CIID

6. Changer de forme
Exemple des polymères photocinétiques
Courtesy Casper Van Oosten
Change in order gives dimensional change
Different textile materials
As discussed in chapter 4.2 three different textile materials were u
composite: polyolefin, polyester and nylon. All three materials see
crystalline materials and the adhesion didn’t seem to differ on first
mechanical testing (see Chapter 4.7) shows that the polyolefin tex
the other textiles, but this was not of influence on the bending. Th
influence on the bending behaviour seemed to be the fibre density
their weight by area. The polyolefin, polyester and nylon materials
and 70 gr/m2
. The bending of the samples is shown in Figure 47.
Figure 47: Bending of samples with different tex
These pictures were taken during the second cycle of illumination.
samples were more or less horizontal but they didn’t revert back to
Textiles photocinétiques, Aurélie Mossé, 2011, en collaboration avec Ele de
Boer et Prf. Dick Broer, Eindhoven Technical University

7. Vêtements connectés
Challenges
• développer un savoir-faire qui ne
soit pas au détriment des qualités
esthétiques
• science/design: mieux collaborer,
adresser l’échelle microscopique et
sensuelle simultanément
• dépasser l’usage de l’électronique
• dépasser l’intéractivité, générer des
intéractions qui respectent le temps
du corps et de la nature

8. Aurélie Mossé l Designer-chercheur et Enseignante l PhD l MA Design for Textile Futures l www.aureliemosse.com l info@aureliemosse.com
Mes vêtements
prennent vie -
17 juin à 18h30
Conférence au Grand Palais, Paris, présentant
les résultats du workshop ENSAD/Orange sur
la thématique des vêtements connectés
Atelier Vêtement, ENSAD, portes ouvertes 2015