The Benefits and Disadvantages of Potash in Steam Reforming

The Benefits and Disadvantages of
Potash In Steam Reforming
Gerard B. Hawkins
Managing Director
www.GBHEnterprises.com

Introduction
 Why do we include potash ?
 What are the benefits ?
 What are the disadvantages ?

Why do we include Potash ?
 Two reasons
• Prevents carbon formation within
 The catalyst
 On the inside wall of the tube
• If carbon is laid down, helps gasification
of carbon
 Potash has to be mobile so that it gets to
the hottest point that the process gas sees
• The inside tube wall

 Catalyst Deactivation
 Carbon Deposition : Thermodynamics & Kinetics
pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100 1200 1300 1400 (°F)
100
Temperature (°C)
High Methane
Concentrations
Increasing Potential for
Carbon Deposition

pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100 1200 1300 1400 (°F)
100
Temperature (°C)
Increasing Rate of
Carbon Deposition

pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100
100
Temperature (°C)
Carbon Deposition Zone
1200 1300 1400 (°F)
Deposition
possible but
rate low
Deposition not favored

pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100
100
Temperature (°C)
CDZ
1200 1300 1400 (°F)
Composition - temperature
profile along reformer tube
No carbon
deposition

pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100
100
Temperature (°C)
CDZ
1200 1300 1400 (°F)
Zone of carbon deposition
30% of tube length

 Carbon Deposition : Prevention
• If carbon deposition occurs by :
CH4 C + 2 H2
• Then carbon deposition rate > carbon removal rate
• Deposition rate is difficult to modify
• Faster carbon removal is possible by leveraging an
additional removal reaction :
C + H2O CO + H2
• Potash acts to increase the rate of this reaction

 Carbon Deposition : Impact of Potash
pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100
100
Temperature (°C)
1200
Faster rate of carbon
removal shrinks CDZ
No carbon deposition
CDZ
1300 1400 (°F)

 In terms of modelling we consider the
margin to carbon formation
 This is defined as the difference between
the
• Equilibrium temperature
• Process gas temperature
 Assumes GOM natural gas
 Care with gases that are heavier than this

 Definition of carbon formation
margin
pH2
2
pCH4
10
1.0
0.1
550 600 650 700 750 800
1100
100
Temperature (°C)
CDZ
1200 1300 1400 (°F)
No carbon
deposition
Margin to Carbon
Formation

600
650
700
750
800
850
0 2 4 6
Distance Down Tube (m)
Temperature(°C)
Inside TWT
Carbon Equilibrium
Margin to Carbon
Formation

600
650
700
750
800
850
0 2 4 6
Temperature(°C)
Base Case Inside TWT
Base Case Carbon
Forming Equilibrium

600
650
700
750
800
850
0 2 4 6
Temperature(°C)
Base Case Inside TWT
Base Case Carbon
Forming Equilibrium
Potash Carbon
Formation

Carbon Formation Margin
-50
0
50
100
150
200
250
0 2 4 6
Temperature(°C)
Base Case Margin

Naphtha Steam Reforming
 Reaction chemistry (Tube inlet)
• Hydrocarbons undergo cracking reactions on hot
surfaces at the tube inlet
• Products of catalytic cracking reactions can form
polymeric carbon
• High strength catalysts required
• Carbon resistant catalysts required
CxHy Cx + y/2H2
CxHy CH4 + H2 + Cx-1H2x-2
Thermal
Catalytic
Polymers

Steam Reforming - Reaction Chemistry
Thermal cracking &
carbon formation
Catalytic cracking and
olefin polymerisation
Steam reforming
reactions
Water gas shift reaction
Heavy
Naphtha
Light
Naphtha

Steam Reforming - Catalyst Design
High strength catalysts
to tolerate carbon
deposition
Carbon resistant
catalysts
High activity catalysts
High activity catalysts
Heavy
Naphtha
Light
Naphtha
or
Mixed
Feeds

So What are the Benefits ?
 Prevents carbon formation in applications
were carbon formation is an issue
 For example
• Highly stressed reformers
 High heat fluxes
 High throughput
• High levels of C2+
 Even then can be insufficient
• Low steam to carbon ratios

What are the Disadvantages ?
 It is assumed that the potash will be
captured on the catalyst in the bottom of the
tubes
 This is not always the case
 In a number of situations there have been
problems
 Usually linked to potash loss
• In some cases fouls the WHB
• Sometimes reaches the HTS
• Can cause SCC of downstream heat
exchangers
• Loss of catalyst strength

 Waste Heat Boiler Fouling
 For NG feeds main issue has been;
• H2 plants are more vulnerable as process
gas temperatures are higher
• Rate of evolution of potash from catalyst
is higher
 Customer X WHB exit temperature increased
at 2°F per day
• Fouling in WHB was 23% potash

 Stress corrosion cracking
 On train at South American Methanol Plant
• 2nd BFW heater (3 in total) suffered from
SCC
• Process gas on shell side
 Design flaw – should have been on tube
side as it is the dirty duty
• Material specified as SS due to supply
issue
 Design flaw – should have been CS
• Huge amount of cracking – due to SCC
 Exchanger irreparable

Effect on WHB
 For Naphtha feeds – a variety of problems on plants
• Again with fouling of WHB
• Older plants have large fouling margin
• Modern plants have had this cut and so have
insufficient surface area
• Requires regular WHB cleaning
• Sometimes bypass valve becomes coated and does
not operate correctly
• Sometimes potash deposited in cold end of WHB
and needs digging out

Effect on HTS
 Most WHB have internal bypass for exit
temperature control – automatic control
 If tubes are fouled, tube exit temperature rises
 Bypass therefore closes to keep WHB exit
temperature constant
 Once bypass fully closes, exit WHB T rises
 Therefore inlet HTS temperature rises
 So CO slip rises
 If HTS catalyst or vessel temperature limit is
reached then plant rate has to be reduced

Effect on HTS
 Potash can also coat the surface of the HTS bed
 Deactivates leading edge of the bed
 Increases CO slip
 Increases DP

Effect on Catalyst
 As potash is removed then strength of catalyst is
reduced
 Causes excessive breakage

Effect on Catalyst
0
20
40
60
80
100
120
140
160
Z203 Z202 Z201 Z101
Catalyst type
kg
Min
Avg
Max

Effect on Catalyst
Carbon Laydown
Test:
Feed
cyclohexane +
steam at 500 oC
and S/C = 3.5
isolate steam
form carbon
remove/inspect
sample after set
times
2
9
15
Timewithoutsteam(mins)
46-3 46-3Q
VSG-Z101 survives where Comp fails

Conclusions
 Potash has many more advantages than
disadvantages
 We have options for the majority of plants
to address carbon formation
 Even the very worst cases
 On some plants there are problems were the
WHB is very sensitive to fouling
A Business Unit of GBH Enterprises, Ltd.

The Benefits and Disadvantages of Potash in Steam Reforming

The Benefits and Disadvantages of Potash in Steam Reforming

Recommandé

Recommandé

Contenu connexe

Tendances

Tendances (20)

En vedette

En vedette (17)

Similaire à The Benefits and Disadvantages of Potash in Steam Reforming

Similaire à The Benefits and Disadvantages of Potash in Steam Reforming (20)

Plus de Gerard B. Hawkins

Plus de Gerard B. Hawkins (20)

Dernier

Dernier (20)

The Benefits and Disadvantages of Potash in Steam Reforming