Page
Griltex Hotmelts for:
Reinforcement of UD-tapes, knitted,
woven and multiply fabrics 3
Thermoplastic Composites 10
2
3. Reinforcement of UD-tapes and fabrics
Especially designed High Performance Polymers
for applications in Composites
made from epoxi-resins and
- Carbon fibers
- Mineral fibers (Glass, Basalt)
- Polymer fibers (Kevlar, Aramide)
- Natural fibers
3
4. Properties
Stabilising of unidirectional filaments
multiply, woven and knitted fabrics
nonwovens
⇒ Better and easier handling
⇒ Antifray
⇒ Gluing of multiple layers to one component
⇒ Production of preforms without additional auxiliaries
4
5. Mechanical Benefits CAI
High positive influence on impact
CAI values rise by 65% - Delamination areas decrease by 85%
CAI
300
250
200
MPa
150
100
50
0
Reference D 2433E D 2351E D 2419E
Delamination area
7000
6000
5000
4000
mm2
3000
2000
1000
0
Reference D 2433E D 2351E D 2419E
18g/m2 Griltex, RTM 6; Testmethod: AITM 1.0010
5
6. Mechanical Benefits Peeling Force
High peeling forces between Griltex High Performance
Polymers and epoxi-resins
⇒ Maintain adhesion from Epoximatrix to fibers.
Peel Strength
160
140
120
100
[N/5cm]
80
60
40
20
0
D 2433E D 2351E D 2419E Standard Flexible Standard PA12 EVA PE
CoPES CoPES CoPA
Bisphenol-A and amine hardener cured at RT on a Griltex polymer film over 16 h
Polymers are insoluble in Epoxi resin
⇒ Maintain the Tg of Epoxi-matrix
6
7. Mechanical Benefit ILSS
ILSS-values increase up to 36%
ILSS - Test
80
70
60
50
MPa
40
30
20
10
0
Reference D 2433E D 2351E D 2419E
23°C 80°C
18g/m2 Griltex; RTM 6;
Test method: ASTM D2344M;
Values at 120°C in preparation
7
8. Technical Data
Griltex Polymer
D 2433E D 2351E D 2419E
Melting range* °C 98-107 95-103 130-140
Glass Transition
°C 18 18 17
temperature*
Melt viscosity**
Pas 450 226 330
(160°C/2.16Kg)
Melt volume rate**
cm3/10' 23 48 32
(160°C/2.16Kg)
Density*** g/cm3 1.31 1.31 1.31
* DSC
** ISO 1133
*** ISO 1183
8
9. Application Techniques
Suitable for all standard application techniques :
→ Hotmelt lamination
→ Powder scattering
→ Powderdot, Pastedot
→ Meltblown
→ Webs
Meltblown hotmelt by standard
spray head.
9
10. Thermoplastic Composites
Matrix material by EMS high performance polymers
→ Easy to handle
→ Short cycle times
→ Reformable by temperature
Applications
→ Orthoses
→ Guards
→ Sports equipment
→ Organosheets
10
11. Technical Data
Griltex Polymer
2A D 1428A
Melting range* °C 120-130 175-180
Glass Transition
°C 15 45
temperature*
Melt viscosity** 560 180
Pas
(°C/2.16Kg) @160°C @ 230°C
Melt volume rate** 18 50
cm3/10'
(°C/2.16Kg) @160°C @ 230°C
Density*** g/cm3 1.02 1.01
Matrix
Use Matrix
Surface
Granules Granules
Availability Powder
Suspension Powder
* DSC
** ISO 1133
*** ISO 1183
11
12. EMS-GRILTECH worldwide
www.emsgriltech.com
info@emsgriltech.com
Europe Americas
EMS-CHEMIE AG EMS-CHEMIE AG (North America) Inc.
Business Unit EMS-GRILTECH Business Unit EMS-GRILTECH
Via Innovativa 1 2060 Corporate Way
CH-7013 Domat/Ems P.O. Box 1717
Phone: +41 81 632 72 02 Sumter, SC 29151-1717, USA
Fax: +41 81 632 74 02 Toll free: +1 877 367 83 23
E-mail: info@emsgriltech.com Phone: +1 803 481 61 90
Fax: +1 803 481 61 29
E-mail: info@us.emsgriltech.com
Asia Japan
EMS-CHEMIE AG (Asia) Ltd. EMS-CHEMIE AG (Japan) Ltd.
Business Unit EMS-GRILTECH Business Unit EMS-GRILTECH
36, Kwang Fu South Road Osaka Office, Umeda Shinmichi Bldg.
Hsin Chu Industrial Park 1-1-5, Dojima, Kita-ku
Fu Kou Hsiang, Hsin Chu Hsien Osaka 530-0003, Japan
Taiwang, R.O.C. Phone: +81 6 6348 1655
Phone: +886 35 983 335 Fax: +81 6 6348 1702
Fax: +886 35 985 731 E-mail: info@jp.emsgriltech.com
E-mail: info@tw.emsgriltech.com
Issued by: Technical Service Coatings + Additives
EMS-CHEMIE AG business unit EMS-GRILTECH
Date: March 2012
Copyright: All rights reserved to EMS-CHEMIE AG.
Any unauthorized copying and publishing is forbidden
GRILTEX is a registered trademark of EMS-CHEMIE AG
12