3. Helium liquefier completed in 1908
in Leiden
Superconductivity first observed in
1911 by Kamerlingh Onnes
Meissner effect discovered in 1933
First superconducting magnet made
in 1954 by George Ynetma
Yttrium Barium Copper Oxide
superconductor with a transition
temperature of 90 K developed in
1987
Figure b: Walther Meissner
Figure a:
Kamerlingh Onnes
(left) and Van der
Waals (right)
4. In perfect conductor resistance has low but
superconductor material has resistance
present exactly zero.
Mostly conductor no need to want
temperature but superconductor occur only
on critical temperature (Tc).
5. Superconductivity is a state of
thermodynamical equilibrium
that affects a material's electric
and magnetic properties.
Superconductivity arises from
an attractive interaction
between pairs of conducting
electrons, and their interaction
with lattice vibrations
It can be achieved by lowering
the material temperature below
its critical temperature
6. In 1957, Bardeen, Cooper, and Schrieffer (BCS) theorized
that superconductivity was the result of electrons
binding to form particles called Cooper pairs
The electrons exchange vibrational lattice energy called
phonons which can result in the electrons becoming
attracted to one another
Recently, antiferromagnetism has been linked to the
explanation of high temperature ceramic
superconductivity
By changing the chemical composition, BaFe2(As1-xPx)2
has been observed to have an internal magnetic critical
point
As the composition is changed, antiferromagnetism
decreases until it disappears, resulting in
superconductivity
7. Below a critical temperature (Tc), the
resistance of a superconducting material
becomes almost zero causing current to
flow indefinitely and with no power loss
No voltage difference is needed to
maintain a current.
Above a current density,
superconductivity is lost in the material.
A supercurrent can flow across an
insulating junction in what is called the
Josephson Effect. Cooper pairs can do
this due to quantum tunneling
8.
9. Superconductors can be classified into two types according to their
interaction with an external magnetic field:
Type I
Type I superconductors expel all magnetic flux
Superconductivity ends when a critical flux is applied. Examples
include mercury, lead, and tin.
10. Type II
Type II superconductors, unlike type I,
have two critical fields.
After the first critical field is reached,
magnetic flux partially penetrates the
material and it enters a state of mixed
normal and superconductivity.
After the second critical flux is passed,
superconductivity abruptly ends. Type
II superconductors usually have higher
critical temperatures.
Examples include YBCO, vanadium,
and BSCCO
11. The phenomena of expelling
magnetic flux experienced by
superconductors is called the
Meissner Effect.
The Meissner Effect can be
understood as perfect
diamagnetism, where the magnetic
moment of the material cancels the
external field or M = - H.
Superconductor
Conductor
12. Some metals become
superconductors at extremely low
temperatures
Some of these include mercury,
lead, tin, aluminum, lead, niobium,
cadmium, gallium, zinc, and
zirconium
Unfortunately, the critical
temperatures are too low for
practical application
For example, Aluminum has a Tc of
only 1.20K, nearly impossible to
reach by conventional methods
13. If a high critical temperature
superconductor is developed that
has a critical temperature that is
higher than HBCCO (133 K), more
practical applications will become
feasible
Electrical power transmission
through superconducting materials
and wire
o Low power loss
o Low voltage required for high
current
o Utilizes less physical space
Computer signal transmission
o Low resistivity allows for computing
speed to increase greatly
14. Yttrium Barium Copper Oxide was the first
superconductor developed with a Tc above
the boiling point of Nitrogen (Tc=90 K).
Thallium Barium Calcium Copper Oxide
has the highest Tc out of all
superconductors (Tc=125 K)
This suggests that the electrons interact
strongly with the positions of copper and
oxygen in the lattice (Cooper pair).
Antiferromagnetism must be eliminated
for superconductivity to appear.
CopperIron
15. Figure :- Example of a superconducting cable. The liquid nitrogen
coolant is part of the cable in order to keep the superconductor wire
below the critical temperature. These cables can greatly reduce the
physical space needed in our electrical infrastructure.
16. Some applications are used today:
o Magnetic Resonance Imaging
o Nuclear Magnetic Resonance Spectroscopy
Future applications can benefit from
interesting magnetic properties displayed by
superconductors
Particle Accelerators
Magnetic Levitation
o High-Speed Magnetic Levitation Trains for
mass transport
o By utilizing levitation, friction between the
train and the track is eliminated
o This can allow trains to increase their speed
dramatically
17. Metal alloys like Nb-Ti, and Nb-Zr are
usually Type II superconductors
Metal Alloys have higher critical
temperatures and magnetic fluxes
than pure metals.
As a consequence of their properties,
they are more useful for practical
applications than pure metals
18. Superconductivity is a state of
thermodynamical equilibrium
where the electrical resistance is
0 and that is achieved at near 0 K
temperatures
Superconducting ceramic
materials have shown the most
promise for future technologies
because of their relatively high
critical temperatures Figure :- Structural
interpretation of a ceramic
superconductor.